AB-3Ti-6Al-6V-2Sn-0.5Cu-0.5Fe titanium bar titanium alloy rod bar titanium round bar
AMS 4928 aviation standards titanium bar
Standard:AMS 4928
Material grade:Beta C (Ti-6Al-6V-2Sn-0.5Cu-0.5Fe)
Diameter:5.0-100mm
Length:6000mm Max
Diameter tolerance:H8, H9, H10, H11, H12, H13K9, K10, K11, K12 or as per clients’ requirements
Ti-6Al-6V-2Sn-0.5Cu-0.5Fe is a kind of titanium alloy.This material have the advantage of light weight, corrosion
resistance of pure titanium itself.And because of these chemical components(V, Sn etc.) added, its hardness
and strength have been greatly increased. The alloy also has good hot workability(including conventional process
performance and superplasticity), and can be welded and machined in various ways. The beta heat treatmentand
is other mal forging of this alloy have achieved rapid development.The alloy is mainly used for the manufacture of
compressor disks, blades, drums and other parts of aircraft engines,and can also be used to manufacture aircraft
structural parts. Through the thermal deformation and heat treatmentin the α-β region, the maximum long-term working temperature of the alloy is 500 ° C. The semi-finished products produced include bars, forgings and die forgings.
Ti-6Al-6V-2Sn-0.5Cu-0.5Fe titanium alloy is a widely used high-temperature titanium alloy with a maximum operating
temperature of 500 ° C.It is mainly used in aircraft engine compressor components such as blades, discs, drums and
shafts. It can also bemade into special-shaped castings. The working conditions of the parts are that they can be used
for 500 hours below 500 ° C and 100 hours below 550 ° C and 1000 hours below 450 ° C in the annealed state, and
can be used for 100 hours below 500 ° C in the strengthening treatment Parts and parts that work at a time below 700 ℃.
| Main chemical composition | Impurities <= |
| Al | Sn | V | Si | Cu | Fe | C | N | H | O | Ti | Others |
| Each | Total |
| 5.5～6.5 | 1.5～2.5 | 5.5～6.5 | 0.20～0.35 | 0.35-1.0 | 0.35-1.0 | 0.08 | 0.04 | 0.015 | 0.20 | Remainder | 0.10 | 0.4 |
| Tensile requirements |
| Grade | Tensile strength(min) | Yeild strength(min) | Elongation(%) |
| ksi | MPa | ksi | MPa |
| Betal C alloy | 149 | 1030 | 131 | 900 | 12 |
| Tolerance of titanium rod diameter |
| Diameter(mm) | h7 | h8 | h9 | h10 | h11 | h12 |
| | Tolerance precision (um) |
| 3Max | 10 | 14 | 25 | 40 | 60 | 100 |
| 3~6 | 12 | 18 | 30 | 48 | 75 | 120 |
| 6~10 | 15 | 22 | 36 | 58 | 90 | 150 |
| 10~18 | 18 | 27 | 43 | 70 | 110 | 180 |
| 18~30 | 21 | 33 | 52 | 84 | 130 | 210 |
| 30~50 | 25 | 39 | 62 | 100 | 160 | 250 |
| 50~80 | 30 | 46 | 74 | 120 | 190 | 300 |
| 80~120 | 35 | 54 | 87 | 140 | 220 | 350 |
| "h"stands for a tolerance range(-x,+0),on the contrary,"H"stands for a tolerance(-0,+X) |
| | Titanium Betal C Bright Bar
Ti-6Al-6V-2Sn-0.5Cu-0.5Fe Titanium Alloy Bright Bar
Titanium Ti-6Al-6V-2Sn-0.5Cu-0.5Fe Bright Bar
AB-3 Titanium Bright Bar
ASTM B4928 Beta C Titanium Bright Bar |
We,Baoji Lihua provide Manufacturer TC (Test Certificate) in accordance to EN 10204/3.1B, Raw Materials Certificate,
100% Radiography Test Report, Third Party Inspection Report. We also provide Standard certificates like EN 10204 3.1
and additional requirement like. NACE MR 01075. FERRIT CONTENT as per norms if requested by clients.
• EN 10204/3.1B,
• Raw Materials Certificate
• 100% Radiography Test Report
• Third Party Inspection Report, etc
We focus on every procedure to assure quality, the package we usually take is pack Titanium Round Bar with environmental poly bags, and then in free fumigation wooden cases or wooden palte. Also can accept customized package such as OEM by negotiation. We offers just about everything to meet your Titanium Round Bar pack requirements. Lot of emphasis is placed on the packing and packaging. The Round Bar are packed in wooden corrugated boxes foiled in plastic wraps and bubble wraps.
Product Tags:
|
|
Round Titanium Alloy Rod AMS4928 AB-3 Beta C Ti-6Al-6V-2Sn-0.5Cu-0.5Fe Images
|